Henan Lite Refractory Material Co.Ltd.

Stone Broken Machine Manufacturers China

Hot Products

  • fire clay brick

    fire clay brick High mechanical strength,Good thermal shock resistance;

  • AZS Bricks

    AZS Bricks AZS arch crown refractory block/brick is manufactured using high quality zirconia and zirconium corundum clinker raw materials with ceramic and chemical bonding.It is shipped underhigh pressure and fired with high temperature with scientific

  • Mullite insulation brick

    Mullite insulation brick Light weight mullite insulating brick is made from pure mullite and adding alumina powder according to different type sintering in high temperature.

  • Refractory cement

    Refractory cement Refractory cement also is called bauxite cement,high alumina cement,aluminate cement. 1.General refractory cement:made by high alumina bauxite and limestone materials 2.High pure refractory cement:made by industrial alumina and limestone Fea

  • High alumina castable

    High alumina castable Made from high alumina aggregate, refractory powder, binders and other additives. Features high mechanical strength,good thermal shock resistance,abrasion resistance, application mainly used as liner of furnace, blast-furnace,heating furnace

Magnesia Bricks



Made from burned magnesia or electric fused magnesia,High pressure forming,high-temperature 1600-1700°C sintering,MgO content is above 91%.
 
►Features
1.High refractoriness,usually the refractoriness is above 2000°C.
2.Refractoriness under load about 1500-1550°C because of poor high-temperature intensity.
3.Strong ability to resist basic (alkaline) slag,can not contact with acid refractory material.
4.Poor Thermal shock resistance,so keep the temperature of furnace stabilized.
5.Poor Volume stability at high temperature,must set aside appropriate expansion joint when laying brick.
6.Strong ability of thermal conductivity,sometime need insulating material.
7.Hydrability, keep product away from moisture during storage.


Technical parameters
Item MZ-97 MZ-95 MZ-93 MZ-91
MgO % ≥97 ≥95 ≥93 ≥91
SiO2 % ≤1.0 ≤2.0 ≤3.5 -
CaO % - ≤2.0 ≤2.0 ≤3.0
Apparent porosity/% ≤16 ≤16 ≤18 ≤18
Cold crushing strength/ Mpa ≥60 ≥60 ≥60 ≥60
Refractoriness under load, 0.2MPa, °C ≥1700 ≥1650 ≥1620 ≥1560
Reheating Linear Change(1650 °C,2h) /% 0~-0.2 0~-0.3 0~-0.4 0~-0.4
 
Application:
Widely used in steelmaking furnace lining;ferroalloy furnace,ferroalloy copper,nickel,lead,zinc,tin etc smelting furnace lining;building material industry lime kiln;glass industry regenerator checke,high temperature calcination kiln,shaft kiln and tunnel kiln.

►Delivery
Package Informations:
1. Packed in a 100cm*100cm fumigated wooden pallet with a waterproof plastic film cover, and tightened with plastic bandages.
2. We can also pack the goods according to your requirements.

Shipping:
1. FEDEX/DHL/UPS/TNT for samples.
2. By Sea for batch goods.
3. Customers specifying freight forwarders or negotiable shipping methods!
4. Delivery Time:3 days for common shape samples;15 days for special shape samples.Within 30 days for batch goods.


Copyright © Henan Lite Refractory Material Co.Ltd. All Rights Reserved.

   
#
Contact Us
Get latest price list here!
Send Messages

If you need more details about our products, please write what you need, we will contact you asap with favorable prices!