Gunnig mix
Item | 1 | 2 | 3 | 4 | 5 | 6 | |
Chemical Composition % | Al2O3 | ≥30 | 42 | 45 | 48 | ≥60 | 66 |
SiO2 | ≥40(SiC) | 40 | 42 | 43 | 24 | 27 | |
Fe2O3 | ≤1.2 | 1.4 | 2.2 | 0.9 | 1.2 | 1.8 | |
Compressive strength MPa | 110°C | 35 | 29 | 29 | 26 | 35 | 58 |
600°C | - | 40 | 27(700°C) | 28 | - | 34(800°C) | |
1000°C | 30 | 31 | 14 | 38 | 30 | - | |
1200°C |
≥55 (1500°C) |
- | 15 | - |
≥55 (1500°C) |
24 | |
Bending Strength MPa | 1000°C | - | 7.0 | 3.1(700°C) | 9 | - | - |
Reheating linear change % | 1000°C | ±0.4 | -0.2 | -0.12 | -0.2 | ±0.41 | -0.3(1200°C) |
Refractoriness under load °C | 4% | 1320 | - | 1314 | - | - | 1300 |
Apparent porosity % | 15.1 | 23.0 | 17.6 | 18.0 | 18.0 | 22.0 | |
Bulk density g/cm3 | 2.35 | 2.06 | 2.14 | 2.32 | ≥2.34 | 2.52 |
Item | 1 | 2 | 3 | 4 | |||||||
Chemical Composition % | MgO | 80 | 96 | 76 | 93 | ||||||
CaO | 3 | - | 10 | 5 | |||||||
SiO2 | 4 | 1.6 | 2.3 | - | |||||||
Bending Strength MPa | 1000°C | 7 | 6.4 | 7.8 | 4.2 | ||||||
1500°C | 6.4 | 8.0 | 9.8 | 5.6 | |||||||
Bonding strength |
1400°C | 2.0 | - | - | 3.4 | ||||||
Bulk density g/cm3 | 2.45 | 2.70 | 2.66 | 2.58 | |||||||
Item | 1 | 2 | 3 | 4 | 5 | ||||||
Refractoriness °C |
≥1530 |
≥1580 | ≥1610 | ≥1580 |
≥1530 |
||||||
Bulk density g/cm3 |
≥1.7 (1200°C) |
≥1.7 (1300°C) |
≥1.8 (1400°C) |
≥1.4 (1300°C) |
≥2.0 (1200°C) |
||||||
Bending Strength MPa |
≥4.0(110°C) ≥0.3(1200°C) |
≥4.0(110°C) ≥0.3(1300°C) |
≥4.0(110°C) ≥0.3(1400°C) |
≥4.0(110°C) ≥0.3(1300°C) |
≥4.0(110°C) ≥1.0(110°C) |
||||||
Reheating linear change % |
±1.0 (1200°C,3h) |
±1.0 (1300°C,3h) |
±1.0 (1400°C,3h) |
±1.0 (1230°C,3h) |
±0.4 (110°C) |
||||||
Thermal conductivity W/(m.k) | ≤0.3(150°C) | ||||||||||
Chemical Composition % |
Al2O3≥30 Fe2O3≤2.0 |
Al2O3≥35 | Al2O3≥45 | Al2O3≥35 |
Al2O3≥55 CaO≤0.5 |
||||||
Service temperature °C | 1200 | 1300 | 1400 | 1300 | 1200 | ||||||
Material | Magnesia | magnesia-calcium1 | magnesia-calcium2 | |
Chemical Composition % | MgO | ≥80 | 65~75 | 55~65 |
SiO2 | 4~6 | ≤5 | ≤5 | |
CaO | - | 8~10 | 20~35 | |
Bulk density g/cm3 | 110°C,24h | 1.6~2.0 | 1.7~2.0 | 1.7~2.0 |
1500°C,3h | 1.7~2.1 | 1.8~2.1 | 1.8~2.1 | |
Bending Strength MPa | 110°C,24h | 1.5~2.0 | 1.6~2.3 | 2.0~2.5 |
1500°C,3h | 4~6 | 5~6 | 5~8 | |
Reheating linear change % | 110°C,24h | -(1.0~1.5) | -(1.2~1.8) | -(1.2~2.5) |
1500°C,3h | -(2.5~3.1) | -(2.0~3.0) | -(2.5~3.2) | |
Thermal conductivity W/(m.k) | 1000°C | ≤0.6 | ≤0.6 | ≤0.6 |
Item | Al2O3-SiC-C based refractory gunning mixes | |||
Chemical Composition % | Al2O3 | 67 | 70 | 22 |
SiC | 14 | 10 | 60 | |
SiO2 | - | - | 15 | |
CaO | - | - | 1.4 | |
F.C | 3 | 3 | - | |
Bulk density g/cm3 | 2.56(110°C) | 2.75(110°C) | 2.5(816°C) | |
2.62(1450°C) | 2.73(1450°C) | |||
Apparent porosity % | 18.5(110°C) | 21.6(110°C) | 16.0(816°C) | |
9.6(1450°C) | 20.0(1450°C) | |||
Strength Mpa |
Bending Strength 16.0(110°C) 19.6(1450°C) |
Bending Strength 2.5(110°C) 6.7(1450°C) |
Compressive strength MPa 83(816°C) |
|
Reheating linear change % | -0.50(1450°C) | +0.11 | -0.1(816°C) | |
water content to mixture % | 6 | 6 | 6 |